Hello all,
Give me a little feedback here on this part regarding the material hardness. The drawing calls out for RC27 min, are you all not able to source this material in a pre-hard condition? We currently source this prehardened to RC30, so I don't think an additional heat treat step is necessary, but give me some feedback, and we can probably make an adjustment.
Thanks